NORTON TAPES (THERMAL
BOND-V2200) |
|
Semi-Rigid polyurethane
-
An open cell structure allows
air and moisture to reach the silicone
permitting optimum curing.
-
Semi-rigid polyurethane foam
substrate is chemically compatible with all
silicones tested.
-
Low thermal conductivity foam
substrate reduces heat transfer and inhibits
condensation on windows, doors and metal
systems.
-
Excellent resistance to
weather, fungi and oxidation.
|
|
 |
|
|
Applications:
-
Structural Silicone Glazing
-
Thermal Break on Storm Windows
and Doors
-
Curtain Wall
-
Die Cut for Vibration
Dampening
|
|
 |
|
|
|
| Typical Physical
Properties |
|
Property |
Test Method |
Value or Rating |
| Density: lbs./cu.ft |
ASTM D-1667 |
22 |
| Force to Compress 10%:psi |
ASTM D-1667 |
16 |
| Hardness:Shore A |
ASTM D-2240 |
30 |
| Tensile Strength:psi |
ASTM D-412 |
130 |
| Elogation:% |
ASTM D 412 |
105 |
| Dynamic Tensile Adhesion:psi (15-minute
dwell) |
NTP-31 |
45 |
Dynamic Shear Adhesion:psi
(15-minute dwell) |
NTP-31 |
30 |
Static Shear
Adhesion:Hours (1psi load) |
NTP-25 |
2000+ |
Thermal Coductivity: K Factor
(BTU(in.)
Sq. Ft. (hr.)°F |
ASTM C-518 |
.55 |
Ultraviolet Resistance:
hrs. exposure |
ASTM G23-69 |
3000 |
| Migratory Staining of Acrylic Enamel:
200 hours of ultraviolet at 140°F |
ASTM D-925 |
No Staining |
|
Recommended Service Temp:-40°F to 180°F
Recommended Application Temp: 60°F to 125°F
NTP is Norton Test Procedure
Parameter values are not guaranteed and will differ from
lot to lot.
For Specification writing , contact Technical Service
Department.
|
| Standard Roll Sizes |
Widths:1/4" to 56"
(6.35mm to 1.4m) |
Color: Black |
3"I.D.Cores |
|
Sealant No. |
**Thickness in. (mm) |
Length ft. (m) |
| V2204 |
1/8 (3.2) |
50 (15.2) |
| V2206 |
3/16 (4.8) |
50 (15.2) |
| V2208 |
1/4 (6.4) |
50 (15.2) |
| V2210 |
5/16 (7.9) |
25 (7.6) |
| V2212 |
3/8 (9.5) |
25 (7.6) |
|
** Metric Sizes Available to minimum quantity orders.
T-Bond II V2200 is a spacer material and is not intended to
be a structural component.Note: The values and
figures provided above are results of tests and subject to
variation. Users are to determine the suitability of our
products.
|